Al/Zn alloy metallized polypropylene safety film with heavy edge

Short Description:

Cores 1、 Material:Plastic. 2、Width:Film Slit Width ±0.3mm. 3、Inner Diameter:75mm +1.0mm/-0.5mm. Outer Diameter of film roll 4.5mm≤W< 10mm 140mm≤D≤185mm 10mm≤W< 25mm 150mm≤D≤185mm 25mm≤W< 50mm 150mm≤D≤240mm 50mm≤W 150mm≤D≤350mm   Specifications of metallized film (MPP Film): Properties Unit Requirements Density g/cm3 0.905±0.005 Thickness μm 3.8 ~ 15 Tensile Strength MD (MPa) ≥100 Elongation at Break MD (%) 40 ~ 200 ...


  • FOB Price: US $0.5 - 9,999 / Piece
  • Min.Order Quantity: 100 Piece/Pieces
  • Supply Ability: 10000 Piece/Pieces per Month
  • Payment Terms: L/C,D/A,D/P,T/T
  • Product Detail

    Product Tags

    Cores
    1、 Material:Plastic.
    2、Width:Film Slit Width ±0.3mm.
    3、Inner Diameter:75mm +1.0mm/-0.5mm.
    Outer Diameter of film roll

    4.5mm≤W<

    10mm

    140mm≤D≤185mm
    10mm≤W<

    25mm

    150mm≤D≤185mm
    25mm≤W<

    50mm

    150mm≤D≤240mm
    50mm≤W 150mm≤D≤350mm

     

    Specifications of metallized film

    (MPP Film):

    Properties

    Unit

    Requirements

    Density

    g/cm3

    0.905±0.005

    Thickness

    μm

    3.8 ~ 15

    Tensile Strength

    MD

    (MPa)

    ≥100

    Elongation at

    Break

    MD

    (%)

    40 ~ 200

    Heat Shrinkage

    MD

    (%)

    ≤5 ( 120°C, 10min)

    Break-dowm

    voltage

    V/μm

    ≥350 ( 23°C, DC )

    Coating square

    resistance

    Ω/□

    (heavy-edge area):3±1

    Coating square

    resistance

    Ω/□

    (nonheavy-edge area):

    7.5±2.5

    Coating square

    resistance

    Ω/□

    2~4

    Dissipation

    Factor

    -

    ≤4×10-4 (20℃,1KHz )

     

    RC

    ΩF

    ≥5×104

    Note:Coating square resistance annotation is

    a typical value, can be customized.Quantity discount is available.

    MPET Film:

    Properties

    Unit

    Requirements

    Density

    g/cm3

    1.34

    Thickness

    μm

    <5 5~12 >12

    Tensile Strength

    MD

    (MPa)

    ≥84 ≥108 ≥120
    Elongation at Break

    MD

    (%)

    ≥22 ≥33 ≥44

    Break-dowm

    voltage

    V/μm

    ≥200(23°C, DC ) ≥250(23°C, DC )

    Heat Shrinkage

    MD

    (%)

    ≤3 ( 120°C, 10min)

    Coating square

    resistance

    Ω/□

    AL 1.5±0.5 ;2.0±0.5;2.5±0.5;3±1

    Coating square

    resistance

    Ω/□

    Zn/AL (6~7.5)±30%

    Dissipation

    Factor

    -

    ≤60×10-4 (20℃,1KHz )

     

    RC

    ΩF

    ≥1×104

    Note:Coating square resistance annotation is

    a typical value, can be customized.Quantity discount is available.

    Packing

    1、Film Rolls are packed and heat-sealed in vacuum

    plastic bags with desiccants inside.

    2、Bags are marked with type lables.

    3、The bags are packed in carton cases.

    4、The cartons are wrapped in wooden cases or

    reinforced carton.

    Storage

    ≤10 Ω/□:6month

    10 ~30Ω/□:3month

    >30Ω/□:1month

    1、Metallized film should be stored in its original

    package with temperature 5 ~ 35℃ and humidity less than 85%RH before using.

    2、Metallized layer is easily oxidized when exposure

    to moisture. Therefore, the film should be used as soon as possible when opened.

    3、The recommended temperature is 15 -25℃ with

    humidity less than 60%RH after opening.

    4、With original sealed package, and stored as

    mentioned above, the storage time can be as following:

    Al metalized Film: 12 months from the delivered

    date.Al/Zn Alloy metalized Film: As Zinc is quite unstable, the storage period(from delivery date) depends on the resistance of

    the film:

    ≤10 Ω/□: 6 months

    10~30Ω/□: 3 months

    >30Ω/□: 1month